Ag修飾對(duì)La_(0.6)Sr_(0.4)Co_(0.2)Fe_(0.8)O_(3-δ)-Er_(0.4)Bi_(1.6)O3復(fù)合陰極電化學(xué)性能的影響
陶瓷學(xué)報(bào)
頁數(shù): 8 2023-10-17
摘要: 為了提高La_(0.6)Sr_(0.4)Co_(0.2)Fe_(0.8)O_(3-δ)(LSCF)-Er_(0.4)Bi_(1.6)O
3(ESB)復(fù)合陰極在氧還原過程的催化活性,采用化學(xué)鍍銀工藝對(duì)復(fù)合陰極進(jìn)行表面修飾,制備了LSCF-ESB-Ag陰極。結(jié)果表明,Ag修飾能夠顯著降低LSCF-ESB復(fù)合陰極的極化阻抗。當(dāng)Ag負(fù)載量為15 wt.%時(shí),LSCF-ESB-Ag陰極的...